Men yangiligiga ishonaman alyuminiy plastinka korxonalar alyuminiy plitalarning umumiy nuqsonlari haqida ko'p narsa bilishmaydi. Xinyitong alyuminiy siz uchun bir nechta umumiy alyuminiy plastinka nuqsonlarini qisqacha tanishtirsin, o'zlarining beparvoligi tufayli korxonaga keraksiz muammo tug'dirmaslik uchun!
1. Plita shakli:
(1) Qattiq qatlam: so'nggi sirt qatlami va chiziq qatlami o'rtasida tartibsiz pog'onali harakat, resulting in uneven end surface. Causes: notekis ignabargli; prokat tegirmonining ochilishi va burilish tarangligini noto'g'ri nazorat qilish; tekislash rulolarini noto'g'ri sozlash, va boshqalar.
(2) Yiqilgan rulon: The roll core is seriously deformed and the roll shape is not round. Cause: Siqish jarayonida noto'g'ri kuchlanish; tashqi kuch zulmi.
(3) Yanal egilish: It is manifested as the bending of the plate shape to one side. Cause: Nivelirning bosimi etarli emas.
(4) To'lqin: A general term for various uneven phenomena formed by uneven deformation of aluminum plates and aluminum strips. The waves generated by the plate and the edge are called edge waves, o'rtada hosil bo'lgan to'lqinlar o'rta to'lqinlar deb ataladi, va o'rta va yon tomonlar orasidagi to'lqinlar na o'rtada, na ikkala tomonda bo'lsa, ikki qovurg'a to'lqinlari deyiladi., which are smaller in size and usually Waves that are circular are called break waves. Causes: Balanssiz rulon oralig'ini sozlash, asossiz rulon shaklini nazorat qilish; notekis soqol va sovutish, alyuminiy plastinkaning notekis deformatsiyasi; o'tish pasayishlarini asossiz taqsimlash, va boshqalar.
2. O'lchamlari:
(1) Qalinligi bardoshliligi: quyida ruxsat etilgan tolerantlik 1.0 ± 1%, yuqorida 1.0 ± 5%, bag'rikenglikdan yagona * 2 marta;
(2) Kenglik tolerantligi: ±0,1MM 3,2MM dan past, ±0,2MM 3,2MM dan yuqori;
(3) Uzunlik bardoshliligi: +5-3MM. The reason for the thickness tolerance, qalinligi o'lchagich muammosi; kenglik tolerantligining sababi, diskni kesishning noto'g'ri sozlanishi; uzunligi bardoshliligining sababi, qirqish mashinasini sozlash muammoli.
3. Yuzaki:
(1) Naqsh: Rulo yuzasidagi tartibsiz rang farqi, chiziqning ajin va singan chizig'i tufayli prokat jarayonida chiziq yuzasida vaqti-vaqti bilan bosiladi..
(2) Chiziqlar: the appearance of scars distributed in bundles on the surface of the aluminum plate. Cause: alyuminiy plastinka qatlamlari orasidagi mexanik yoki sun'iy dislokatsiya.
(3) Chetlarning burishishi: Rolling yoki qirqishdan keyin, tasmaning cheti egilgan.
(4) Korroziya: It is manifested as point-like or flaky white spots or black spots on the surface of the aluminum plate. Cause: Kislota, ishlab chiqarish jarayonida kiritilgan gidroksidi yoki suv, qadoqlash, tashish va saqlash.
(5) Sirtda yog'li dog ': it is manifested as dirt on the surface. Cause: Sovutish moyi iflos va havo puflash kuchli emas.
(6) Chiziqlar: There are line-distributed scars on the surface of the aluminum plate. Causes: Yo'naltiruvchi plastinka tekis o'ralgan holda alyuminiyga yopishib qoladi yoki chiqib ketadi; qirqish jarayonida chizish paydo bo'ladi; noto'g'ri qo'lda tekshirish va ko'tarish.
(7) Yon egilish: the longitudinal sides of the plate and belt are in a non-straight state that is bent to one side. Causes: Prokat tegirmonining har ikki uchidagi pasayish miqdori har xil;
(8) Sirtdagi qora dog'lar: There are needle-shaped black spots on the surface of the aluminum plate. Cause: Pechdagi suyuqlik toza emas.
4. Mexanik xususiyatlar:
(1) The hardness is not enough. Sabab, material/tarkib, issiqlik bilan ishlov berish jarayoni.
(2) Shtamplash va yorilish, hard or soft. Material or condition issues.
(3) Boshqa nuqsonlar: Oksidlanishdan keyin suv to'lqinlanadi, qora va oq chiziqlar; yuzasida quyuq gullar; yuzasida yorqin emas, va boshqalar.