Vigezo
- Jina linalolingana: 50/52, a5052, aa5052, a5052p etc
- Hasira: Laini AU, H14, H18, H19, H22, H23, H24, H26, H28, H32, H34, H36, H38, H44, H111, H112, H114 etc
Kulingana na aina ya bidhaa, inaweza kugawanywa katika
- 5052 alloy metal aluminum sheet palte
- 5052 coil ya alumini ya aloi ya chuma
- 5052 sahani ya alumini ya aloi ya chuma
- 5052 alloy chuma alumini mzunguko
Kulingana na matibabu ya uso, inaweza kugawanywa katika
- Rangi 5052 aloi ya alumini ya chuma
- Imepachikwa 5052 aloi ya alumini ya chuma
- Mirror 5052 aloi ya alumini ya chuma
- Anodized 5052 aloi ya alumini ya chuma
5052 aloi ya alumini ya chuma is a common alloy in 5000 mfululizo wa aloi ya alumini ya chuma. The 5052 aluminum is highly resistant to corrosion. It is an alloy that contains 0.25 asilimia chromium na 2.5 asilimia ya magnesiamu. It’s widely used because of its formability and durability. It has high fatigue and medium static strength. It can be used in marine grade environments without worry of corrosion. This metal also has excellent thermal conductivity and low density, which is commonly found with other aluminum alloys. Its fatigue properties and endurance limit are excellent. Kikomo cha uvumilivu ni 125 MPa in an H34 temper and 115 MPa in an H32 temper.
5052 aluminum alloy is Al-Mg system rustproof aluminum, compared with 3A21, 5052 strength is higher, especially with high fatigue strength; similar to 3A21, plastiki ya juu na upinzani wa kutu; matibabu ya joto haiwezi kuimarishwa, good weldability with contact welding and hydrogen atomic welding, argon arc welding has the tendency of crystalline cracking; alloy in the cold hardening and semi-cold hardening state machinability is good, annealed state can be Poor machinability, inang'aa.
The features of 5052 aloi ya alumini ya chuma
- Aluminum alloy with Mg as the main alloying element. The magnesium content is between 3-5%. Also can be called aluminum-magnesium alloy.
- Not heat treated and strengthened.
- Density is small (5052 density is 2.68). The weight of aluminum-magnesium alloy in the same area is lower than other series. The strength is higher than 1 na 3 mfululizo, and it is a medium and high strength aluminum alloy with good fatigue and welding performance. High tensile strength and high elongation.
- better resistance to marine atmospheric corrosion.
5052 metal aluminum alloy belongs to hot rolled aluminum sheet series, so it can do deep processing of oxidation.
5052 metal aluminum alloy chemical composition:
Vipengele | Na | Fe | Cu | Mhe | Mg | Cr | Zn | Ya | Wengine | Al | ||
Maudhui | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | 0.1 | - | 0.15 | Kubaki |
5052 metal aluminum alloy property
5052 metal aluminum alloy mechanical properties
- Tensile strengthb(MPa)173~244
- Conditional yield strength∞02(MPa)270
- Density 2.68g/cm3
- Specimen size: unene wote wa ukuta
Kumbuka:Mali ya mitambo ya longitudinal ya zilizopo kwenye joto la kawaida
5052 aluminum has great workability and is readily machinable and weldable. Nguvu yake ya juu ya uchovu na nguvu tuli ya kati, pamoja na upinzani bora wa kutu, kuifanya iwe maarufu kwa matumizi katika anga za baharini. Kama vile aloi zingine za alumini, daraja hili la alumini ina conductivity bora ya mafuta. Ili kuimarisha aloi hii, kazi ya baridi inapaswa kutumika, kwani kazi ya joto haiwezi kufikia hili. Ina mipaka bora ya uvumilivu na mali ya uchovu.
Aloi Hasira |
Imebainishwa
unene |
Tensile nguvu |
Mazao nguvu |
Kurefusha | ||||||||
(MPa) | (MPa) | (%) | ||||||||||
5052 HO/H111 | 0.3~0.63mm | 173-213 | min66 | min 15 | ||||||||
0.63~1.2mm | min 17 | |||||||||||
1.2~ 6.3mm | min 19 | |||||||||||
6.3~ 50mm | min 18 | |||||||||||
5052/H32 au 5052 H22 | 0.4~0.63mm | 214-262 | min159 | min 4 | ||||||||
0.63~1.2mm | min 5 | |||||||||||
1.2~ 6.3mm | min 7 | |||||||||||
6.3~ 50mm | min 11 | |||||||||||
5052/H34 au 5052 H24 | 0.4~0.63mm | 235-282 | Dakika 180 | min 3 | ||||||||
0.63~1.2mm | min 4 | |||||||||||
1.2~ 6.3mm | min 6 | |||||||||||
6.3~ 50mm | min 10 | |||||||||||
5052/H36 au 5052 H26 | 0.1~0.32mm | 256-303 | min200 | min 2 | ||||||||
0.32~0.63mm | min 3 | |||||||||||
0.63~ 4 mm | min 4 | |||||||||||
5052/H38 au 5052 H28 | 0.15~0.32mm | min269 | min221 | min 2 | ||||||||
0.32~0.63mm | min 3 | |||||||||||
0.63~3.2mm | min 4 |
The applications of 5052 aloi ya alumini ya chuma
5052 aluminum alloy belongs to the Al-Mg system alloy, which is used in a wide range and especially It has good corrosion resistance, weldability bora, kazi nzuri ya baridi na nguvu ya kati.
5052 alloy is used to require good formability and corrosion resistance, high fatigue limit, weldability nzuri, medium static load components such as aircraft fuel and have oil material conduit, fuel tanks and a variety of marine and land cloud equipment parts, cold stamping parts, sheet metal work products, street lamp pillars; materials used as rivets or welding rod.
Kipengele kikuu cha aloi ya 5052 metal aluminum alloy is magnesium, which has good forming and processing properties, upinzani wa kutu, weldability, nguvu ya kati, kutumika katika utengenezaji wa matangi ya mafuta ya ndege, mabomba ya mafuta, and sheet metal parts of transportation vehicles, meli, vyombo, mabano ya taa za barabarani na rivets, bidhaa za vifaa, nyumba za umeme, na kadhalika.
5052 metal aluminum alloy heat treatment specifications
- homogenization annealing heating 440C holding time 12 ~ 14h air cooling.
- rapid annealing: inapokanzwa 350 ~ 410C insulation time 30 ~ 120min; empty or water cooling
- high-temperature annealing: inapokanzwa 350 ~ 420 ℃ finished thickness ≥ 6mm or <6mm, insulation time of 2 - 10min or 10 ~ 30mn; baridi ya hewa
- low-temperature annealing: inapokanzwa 250 ~ 300 ° C or 150 ~ 180 °C; holding time of 1 ~ 2h, air-cooled.