Kirish 1060 Alyuminiy plitalar plitasi
1060 alyuminiy plitalar plitasi tegishli 1000 seriyali alyuminiy qatlam, bu juda o'xshash 1050 dan ortiq alyuminiy qotishmasi 0.1% og'irligi bo'yicha alyuminiy.
Ikkalasi ham 1050 va 1060 Huawei AL alyuminiy plitasi, ISO standartlariga javob beradi, lekin ular turli ASTM standartlarini qamrab oladi. 1060 alyuminiy qotishmasi mavjud 0.05% cooper, shunday, its conductivity is 55%.
Bundan tashqari, 1060 aluminum sheet is relatively low strength, essentially pure aluminum alloy with many different tempers, kabi O (tavlangan), H12, H14, H16, H18, va boshqalar. what’s more, other aluminum sheets belonging to the commercially pure wrought family are available, shu jumladan 1050, 1070, 1100 and so on and so forth.
1060 alyuminiy
Issiq sotish 1 seriyali alyuminiy plastinka
- 1050 alyuminiy qatlam
- 1060 alyuminiy qatlam
- 1070 alyuminiy qatlam
- 1100 alyuminiy qatlam
- 1200 alyuminiy qatlam
1060 aluminum sheet feature
1060 aluminum sheet Has good elongation and tensile strength, can satisfy completely the requirements of conventional processing (shtamplash, stretch) yuqori shakllanish qobiliyati.
For industrial pure aluminum, high plasticity, korroziyaga qarshilik, elektr o'tkazuvchanligi, va issiqlik o'tkazuvchanligi, but strength is low, heat treatment can not be improved machinability is bad; Gas welding, hydrogen welding, and resistance welding are not easy to brazing; Under various pressure processing and extension, egilish.
1060 aluminum sheet applications
1060 aluminum sheet is widely used in signs, bilbordlar, binoning tashqi bezagi, avtobus korpusi, baland binolar va zavod devori tanasi bezaklari, oshxona lavabosi, chiroq ushlagichi, do'zax barglari, elektron qismlar, kimyoviy uskunalar, mexanik qismlar, choyshab yoki yigiruv konkav buyumlarni chuqur chizish, payvandlash qismi, issiqlik almashtirgich, soat yuzasi va plastinka, plastinka, oshxona anjomlari, bezaklar, aks ettiruvchi uskunalar, making car heat shield, chemical and marine equipment, va boshqalar.
applications of 1060 alyuminiy qatlam
ning texnik xususiyatlari 1060 alyuminiy plitalar
Ekvivalent qotishma nomi :a1060 , 1060a, aa1060 , 1060aa, al1060, al1060a, a 1060, aa 1060, jis a1060p, al1060 class, aw1060, en1060 grade etc
Jahl : Yumshoq HO (h0), H11, H12, H13, H14, H15, H16, H17, H18, H19, H20, H21, H22, H23, H24, H25, H26, H27, H28, H29, H30, H31, H32, H33, H34, H35, H36, H37, H38, H39, H46, H48, H111, H112, H114, H116, H131, H321, va boshqalar
Thicknesses: 0.15mm, 0.4mm, 0.6mm, 1mm, 2mm, 5mm, 10mm, 20mm, 42mm va boshqalar
Standard size: 4x8, 4x10, 5x10 etc
Yuzaki ishlov berish: mirror polished, anodlangan, taralgan, rangli qoplangan, va boshqalar
1060 alyuminiy qatlam kimyoviy tarkibi
| Elementlar | Va | Fe | Cu | Mn | Mg | Cr | Zn | Of | Boshqalar | Al | |||
| Tarkib (maks) | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | - | 0.05 | 0.03 | 0.15 | Qoling | |||
ning jismoniy xususiyatlari 1060 alyuminiy plastinka
| Qotishma temperaturasi | Belgilangan | Kuchlanish | Yo'l bering | Cho'zilish(%) |
| Qalinligi(ichida.) | kuch(ksi) | kuch(ksi) | ||
| 1060-O(tavlangan) | 0.006-0.019 | 8.0-14.0 | 2.5 | Min 15 |
| 0.020-0.050 | Min22 | |||
| 0.051-3.000 | Min 25 | |||
| 1060-H12/1060-H22 | 0.017-0.050 | 11.0-16.0 | 9 | Min 6 |
| 0.051-2.000 | Min 12 | |||
| 1060-H14/1060-H24 | 0.006-0.019 | 12.0-17.0 | 10 | Min 1 |
| 0.020-0.050 | Min 5 | |||
| 0.051-1.000 | Min 10 | |||
| 1060-H16/1060-H26 | 0.006-0.019 | 14.0-19.0 | 11 | Min 1 |
| 0.020-0.050 | Min 4 | |||
| 0.051-0.162 | Min 5 | |||
| 1060-H18/1060-H28 | 0.006-0.019 | Min16.0 | Min 12.0 | Min 1 |
| 0.020-0.050 | Min3 | |||
| 0.051-0.128 | Min 4 | |||
| 1060-H112 | 0.250-0.499 | Min 11.0 | Min 7.0 | Min 10 |
| 0.500-1.000 | Min10.0 | Min 5.0 | Min 20 | |
| 1.001-3.000 | Min9.0 | Min 4.0 | Min 25 |
1060 Aluminum sheet Machinability
The machinability of AL 1060 aluminum is fair to poor, especially in soft temper conditions.
In the harder (cold worked) tempers such as H16 and H18, the machining characteristics are improved. Either carbide or high-speed steel tooling may be used and the use of lubricants is recommended, although some cutting may be done dry.
Issiqlik bilan ishlov berish jarayoni 1060 alyuminiy qatlam
Fast annealing: the heating temperature is 350~410 degrees centigrade; with the effective thickness of the material, the heat preservation time is between 30 and 120min; cooling in air or water.
High-temperature annealing: the heating temperature is 350~500 DEG C; if the finished thickness is not less than 6mm, the holding time is 10 ~ 30min, if the thickness is less than 6mm, heat until all the sheet is hot, cooling in the air.
Low-temperature annealing: the heating temperature is 150~250 degrees centigrade; the heat preservation time is 2 ~ 3H; cooling in air or water.
heat treatment process of 1060 alyuminiy qatlam
1060 alyuminiy qatlamli qadoqlash
1060 Aluminum Sheet of the packaging meets the export standard. Plastik plyonka va jigarrang qog'oz mijozlarning ehtiyojlariga ko'ra qoplanishi mumkin. Mahsulotlarni etkazib berish paytida shikastlanishdan himoya qilish uchun yog'och quti yoki yog'och taglik qabul qilinadi.
1060 alyuminiy qatlamli qadoqlash
1060 alyuminiyga qarshi 6061 alyuminiy
Alloy Composition |
|||||||||||
| Al | Fe | Va | Zn | Cu | V | Mn | Of | Mg | Cr | Qoldiqlar | |
| 1060 alyuminiy | 99.6-100 | 0-0.35 | 0-0.25 | 0-0.05 | 0-0.05 | 0-0.05 | 0-0.03 | 0-0.03 | 0-0.03 | - | - |
| 6061 alyuminiy | 95.9-98.6 | 0-0.7 | 0.4-0.8 | 0-0.25 | 0.15-0.4 | - | 0-0.15 | 0-0.15 | 0.8-1.2 | 0.04-0.35 | 0-0.15 |
Mexanik xususiyatlar |
||||||||
| Elastik (Yoshlar, Kuchlanish) Modul(Gpa) | Charchoq kuchi(MPa) | Kesish moduli(Gpa) | Mustahkamlik chegarasi: Yakuniy (UTS)(MPa) | Tanaffusdagi cho'zilish(%) | Puasson nisbati | Kesish kuchi(MPa) | Mustahkamlik chegarasi: Yo'l bering (Isbot)(MPa) | |
| 1060 alyuminiy | 68 | 15 - 50 | 26 | 67 - 130 | 1.1 - 30 | 0.33 | 42 - 75 | 17 - 110 |
| 6061 alyuminiy | 69 | 58 - 110 | 26 | 130 - 410 | 3.4 - 20 | 0.33 | 84 - 210 | 76 - 370 |