Кіріспе 1060 Алюминий парағы
1060 aluminum sheet plate belongs to 1000 сериялы алюминий парағы, which is pretty similar to 1050 aluminum alloy with more than 0.1% of aluminum by weight.
Екеуі де 1050 және 1060 aluminum sheet of Huawei AL, lives up to ISO standards, but they cover different ASTM standards. 1060 aluminum alloy contains 0.05% cooper, осылайша, its conductivity is 55%.
Сонымен қатар, 1060 aluminum sheet is relatively low strength, essentially pure aluminum alloy with many different tempers, сияқты О (күйдірілген), H12, H14, H16, H18, т.б. what’s more, other aluminum sheets belonging to the commercially pure wrought family are available, оның ішінде 1050, 1070, 1100 and so on and so forth.
1060 алюминий
Ыстық сату 1 сериялы алюминий пластина
- 1050 алюминий парағы
- 1060 алюминий парағы
- 1070 алюминий парағы
- 1100 алюминий парағы
- 1200 алюминий парағы
1060 aluminum sheet feature
1060 aluminum sheet Has good elongation and tensile strength, can satisfy completely the requirements of conventional processing (штамптау, stretch) high formability.
For industrial pure aluminum, high plasticity, коррозияға төзімділік, электр өткізгіштік, және жылу өткізгіштік, but strength is low, heat treatment can not be improved machinability is bad; Gas welding, hydrogen welding, and resistance welding are not easy to brazing; Under various pressure processing and extension, иілу.
1060 алюминий парақ қолданбалары
1060 aluminum sheet is widely used in signs, билбордтар, building exterior decoration, bus body, tall buildings and factory wall body adornment, kitchen sink, lamp holder, fan blade, electronic parts, химиялық жабдықтар, механикалық бөлшектер, deep drawing of sheet or spinning concave ware, welding part, жылу алмастырғыш, clock surface and plate, табақ, ас үй ыдыстары, ornaments, reflective equipment, making car heat shield, chemical and marine equipment, т.б.
applications of 1060 алюминий парағы
Техникалық сипаттамалары 1060 алюминий парақтары
Equivalent alloy name :a1060 , 1060а, aa1060 , 1060аа, al1060, al1060a, а 1060, аа 1060, jis a1060p, al1060 class, aw1060, en1060 grade etc
Температура : Жұмсақ HO (h0), H11, H12, H13, H14, H15, H16, H17, H18, H19, H20, H21, H22, H23, H24, H25, H26, H27, H28, H29, H30, H31, H32, H33, H34, H35, H36, H37, H38, H39, H46, H48, H111, H112, H114, H116, H131, H321, т.б
Thicknesses: 0.15мм, 0.4мм, 0.6мм, 1мм, 2мм, 5мм, 10мм, 20мм, 42мм т.б
Standard size: 4x8, 4x10, 5x10 etc
Беттік өңдеу: mirror polished, анодталған, щеткалы, түсті боялған, т.б
1060 алюминий парағының химиялық құрамы
| Элементтер | Және | Фе | Cu | Mn | Mg | Cr | Zn | Оның | Басқалар | Әл | |||
| Мазмұны (макс) | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | - | 0.05 | 0.03 | 0.15 | Қалыңыз | |||
Физикалық қасиеттері 1060 алюминий пластина
| Қорытпа температурасы | Көрсетілген | Созылу | Өткізіп жібер | Ұзарту(%) |
| Қалыңдығы(жылы.) | күш(ksi) | күш(ksi) | ||
| 1060-О(күйдірілген) | 0.006-0.019 | 8.0-14.0 | 2.5 | Мин 15 |
| 0.020-0.050 | Min22 | |||
| 0.051-3.000 | Мин 25 | |||
| 1060-H12/1060-H22 | 0.017-0.050 | 11.0-16.0 | 9 | Мин 6 |
| 0.051-2.000 | Мин 12 | |||
| 1060-H14/1060-H24 | 0.006-0.019 | 12.0-17.0 | 10 | Мин1 |
| 0.020-0.050 | Мин 5 | |||
| 0.051-1.000 | Мин 10 | |||
| 1060-H16/1060-H26 | 0.006-0.019 | 14.0-19.0 | 11 | Мин1 |
| 0.020-0.050 | Мин 4 | |||
| 0.051-0.162 | Мин 5 | |||
| 1060-H18/1060-H28 | 0.006-0.019 | Min16.0 | Мин 12,0 | Мин1 |
| 0.020-0.050 | Мин 3 | |||
| 0.051-0.128 | Мин 4 | |||
| 1060-H112 | 0.250-0.499 | Мин 11,0 | Мин 7,0 | Мин 10 |
| 0.500-1.000 | Min10.0 | Мин 5,0 | Мин 20 | |
| 1.001-3.000 | Min9.0 | Мин 4,0 | Мин 25 |
1060 Aluminum sheet Machinability
The machinability of AL 1060 aluminum is fair to poor, especially in soft temper conditions.
In the harder (cold worked) tempers such as H16 and H18, the machining characteristics are improved. Either carbide or high-speed steel tooling may be used and the use of lubricants is recommended, although some cutting may be done dry.
Термиялық өңдеу процесі 1060 алюминий парағы
Fast annealing: the heating temperature is 350~410 degrees centigrade; with the effective thickness of the material, the heat preservation time is between 30 and 120min; cooling in air or water.
High-temperature annealing: the heating temperature is 350~500 DEG C; if the finished thickness is not less than 6mm, the holding time is 10 ~ 30min, if the thickness is less than 6mm, heat until all the sheet is hot, cooling in the air.
Low-temperature annealing: the heating temperature is 150~250 degrees centigrade; the heat preservation time is 2 ~ 3H; cooling in air or water.
heat treatment process of 1060 алюминий парағы
1060 алюминий парақ орау
1060 Aluminum Sheet of the packaging meets the export standard. Пластикалық пленка мен қоңыр қағазды тұтынушылардың қажеттіліктері бойынша жабуға болады. Өнімдерді жеткізу кезінде зақымданудан қорғау үшін ағаш қорап немесе ағаш паллет қабылданады.
1060 алюминий парақ орау
1060 алюминийге қарсы 6061 алюминий
Alloy Composition |
|||||||||||
| Әл | Фе | Және | Zn | Cu | В | Mn | Оның | Mg | Cr | Қалдықтар | |
| 1060 алюминий | 99.6-100 | 0-0.35 | 0-0.25 | 0-0.05 | 0-0.05 | 0-0.05 | 0-0.03 | 0-0.03 | 0-0.03 | - | - |
| 6061 алюминий | 95.9-98.6 | 0-0.7 | 0.4-0.8 | 0-0.25 | 0.15-0.4 | - | 0-0.15 | 0-0.15 | 0.8-1.2 | 0.04-0.35 | 0-0.15 |
Механикалық қасиеттері |
||||||||
| Серпімді (Жастық, Созылу) Модуль(GPa) | Шаршау күші(МПа) | Кесу модулі(GPa) | Созылу күші: Түпкілікті (UTS)(МПа) | Үзіліс кезінде созылу(%) | Пуассон қатынасы | Ығысу күші(МПа) | Созылу күші: Өткізіп жібер (Дәлелдеу)(МПа) | |
| 1060 алюминий | 68 | 15 - 50 | 26 | 67 - 130 | 1.1 - 30 | 0.33 | 42 - 75 | 17 - 110 |
| 6061 алюминий | 69 | 58 - 110 | 26 | 130 - 410 | 3.4 - 20 | 0.33 | 84 - 210 | 76 - 370 |
1060 aluminum sheet production packaging and inventory
Huawei алюминий бағасы
| Күн | LME | LME апталық бағасы | 2023-04 LME орташа | 2023-04 SMM орташа |
| 2023-05-03 | 2330$ | 2333.3$ | 2341.00$ | 2712.08$ |
| 2023-05-02 | 2353$ | |||
| 2023-04-28 | 2342$ | |||
| 2023-04-27 | 2302$ | |||
| 2023-04-26 | 2339.5$ | |||
| Жазбалар
1. Бағалар жаңартылады 10:00 жұмыс күндерімін. |
||||