Introductie van 1060 Aluminium plaat
1060 aluminium plaat behoort tot 1000 serie aluminium plaat, wat redelijk vergelijkbaar is met 1050 aluminiumlegering met meer dan 0.1% van aluminium per gewicht.
Beide 1050 En 1060 aluminiumplaat van Huawei AL, voldoet aan de ISO-normen, maar ze bestrijken verschillende ASTM-normen. 1060 aluminiumlegering bevat 0.05% kuiper, dus, its conductivity is 55%.
Daarnaast, 1060 aluminum sheet is relatively low strength, essentially pure aluminum alloy with many different tempers, such as O (gegloeid), H12, H14, H16, H18, enz. what’s more, other aluminum sheets belonging to the commercially pure wrought family are available, inbegrepen 1050, 1070, 1100 and so on and so forth.
1060 aluminium
Hot selling 1 serie aluminium plaat
- 1050 aluminium plaat
- 1060 aluminium plaat
- 1070 aluminium plaat
- 1100 aluminium plaat
- 1200 aluminium plaat
1060 aluminum sheet feature
1060 aluminum sheet Has good elongation and tensile strength, can satisfy completely the requirements of conventional processing (stempelen, stretch) high formability.
For industrial pure aluminum, high plasticity, corrosiebestendigheid, elektrische geleidbaarheid, en thermische geleidbaarheid, but strength is low, heat treatment can not be improved machinability is bad; Gas welding, hydrogen welding, and resistance welding are not easy to brazing; Under various pressure processing and extension, buigen.
1060 aluminum sheet applications
1060 aluminum sheet is widely used in signs, billboards, building exterior decoration, bus body, tall buildings and factory wall body adornment, kitchen sink, lamp holder, fan blade, electronic parts, chemische apparatuur, mechanische onderdelen, deep drawing of sheet or spinning concave ware, welding part, heat exchanger, clock surface and plate, bord, keukengerei, ornaments, reflective equipment, making car heat shield, chemical and marine equipment, enz.
applications of 1060 aluminium plaat
Specificaties van 1060 aluminium platen
Equivalente legeringsnaam :a1060 , 1060A, aa1060 , 1060aa, al1060, al1060a, A 1060, aa 1060, jis a1060p, al1060 class, aw1060, en1060 grade etc
Woedeaanval : Zachte HO (h0), H11, H12, H13, H14, H15, H16, H17, H18, H19, H20, H21, H22, H23, H24, H25, H26, H27, H28, H29, H30, H31, H32, H33, H34, H35, H36, H37, H38, H39, H46, H48, H111, H112, H114, H116, H131, H321, enz
Thicknesses: 0.15mm, 0.4mm, 0.6mm, 1mm, 2mm, 5mm, 10mm, 20mm, 42mm enz
Standard size: 4x8, 4x10, 5x10 etc
Oppervlaktebehandeling: mirror polished, geanodiseerd, geborsteld, kleur gecoat, enz
1060 aluminum sheet chemical composition
| Elementen | En | Fe | Cu | Mn | mgr | Cr | Zn | Van | Anderen | Al | |||
| Inhoud (maximaal) | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | - | 0.05 | 0.03 | 0.15 | Blijven | |||
Fysische eigenschappen van 1060 aluminium plaat
| Alloy Temper | Specified | Tensile | Yield | Verlenging(%) |
| Dikte(in.) | kracht(ksi) | kracht(ksi) | ||
| 1060-O(gegloeid) | 0.006-0.019 | 8.0-14.0 | 2.5 | Min15 |
| 0.020-0.050 | Min22 | |||
| 0.051-3.000 | Min25 | |||
| 1060-H12/1060-H22 | 0.017-0.050 | 11.0-16.0 | 9 | Min6 |
| 0.051-2.000 | Min12 | |||
| 1060-H14/1060-H24 | 0.006-0.019 | 12.0-17.0 | 10 | Min1 |
| 0.020-0.050 | Min5 | |||
| 0.051-1.000 | Min10 | |||
| 1060-H16/1060-H26 | 0.006-0.019 | 14.0-19.0 | 11 | Min1 |
| 0.020-0.050 | Min4 | |||
| 0.051-0.162 | Min5 | |||
| 1060-H18/1060-H28 | 0.006-0.019 | Min16.0 | Min12.0 | Min1 |
| 0.020-0.050 | Min3 | |||
| 0.051-0.128 | Min4 | |||
| 1060-H112 | 0.250-0.499 | Min11.0 | Min7.0 | Min10 |
| 0.500-1.000 | Min10.0 | Min5.0 | Min20 | |
| 1.001-3.000 | Min9.0 | Min4.0 | Min25 |
1060 Aluminum sheet Machinability
The machinability of AL 1060 aluminum is fair to poor, especially in soft temper conditions.
In the harder (cold worked) tempers such as H16 and H18, the machining characteristics are improved. Either carbide or high-speed steel tooling may be used and the use of lubricants is recommended, although some cutting may be done dry.
The heat treatment process of 1060 aluminium plaat
Fast annealing: the heating temperature is 350~410 degrees centigrade; with the effective thickness of the material, the heat preservation time is between 30 and 120min; cooling in air or water.
High-temperature annealing: the heating temperature is 350~500 DEG C; if the finished thickness is not less than 6mm, the holding time is 10 ~ 30min, if the thickness is less than 6mm, heat until all the sheet is hot, cooling in the air.
Low-temperature annealing: the heating temperature is 150~250 degrees centigrade; the heat preservation time is 2 ~ 3H; cooling in air or water.
heat treatment process of 1060 aluminium plaat
1060 aluminum sheet packing
1060 Aluminum Sheet of the packaging meets the export standard. Plastic film and brown paper can be covered at customers’ needs. A wooden case or wooden pallet is adopted to protect products from damage during delivery.
1060 aluminum sheet packing
1060 aluminum vs 6061 aluminium
Alloy Composition |
|||||||||||
| Al | Fe | En | Zn | Cu | V | Mn | Van | mgr | Cr | Residuen | |
| 1060 aluminium | 99.6-100 | 0-0.35 | 0-0.25 | 0-0.05 | 0-0.05 | 0-0.05 | 0-0.03 | 0-0.03 | 0-0.03 | - | - |
| 6061 aluminium | 95.9-98.6 | 0-0.7 | 0.4-0.8 | 0-0.25 | 0.15-0.4 | - | 0-0.15 | 0-0.15 | 0.8-1.2 | 0.04-0.35 | 0-0.15 |
Mechanische eigenschappen |
||||||||
| Elastic (Young's, Tensile) Modulus(GPa) | Vermoeidheid Sterkte(MPa) | Shear Modulus(GPa) | Treksterkte: Ultiem (UTS)(MPa) | Verlenging bij breuk(%) | Poisson's Ratio | Shear Strength(MPa) | Treksterkte: Yield (Proof)(MPa) | |
| 1060 aluminium | 68 | 15 - 50 | 26 | 67 - 130 | 1.1 - 30 | 0.33 | 42 - 75 | 17 - 110 |
| 6061 aluminium | 69 | 58 - 110 | 26 | 130 - 410 | 3.4 - 20 | 0.33 | 84 - 210 | 76 - 370 |