1200 aluminum alloy sheet introduction
1200 aluminum plate is the industrial pure aluminum, бо пластикии баланд, муқовимат ба зангзании, гузаронандагии электрикӣ ва гармӣ, вале кувваи паст, heat treatment can not be strengthened, machinability is not good.
1200 варақи алюминий
1200 aluminum sheet plate chemical composition
| Хӯла | Ва | Фе | Cu | Мн | Mg | Cr | Зн | Аз | Дар | Дигарон | Ал |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 1200 | ≤0,15 | ≤0,25 | ≤0,05 | 0.10 | - | - | ≤0,10 | ≤0,05 | - | ≤0,05 | 99.00 |
1200 aluminium-sheets
1200 aluminum sheet plate mechanical properties
| Tensile strength σb | Elongation δ10 | Elongation δ5 | Шарҳ |
|---|---|---|---|
| 75～105MPa | ≥22% | ≥25% | Longitudinal mechanical properties of tubes at room temperature |
1200 хусусиятҳои варақи алюминий
Дар 1200 aluminum alloy plate is a typical hard aluminum alloy in the aluminum-copper-magnesium series. Its composition is relatively reasonable and its comprehensive performance is better. Many countries produce this alloy, which is the largest amount of duralumin. The characteristics of this alloy are high strength, certain heat resistance, and can be used as working parts below 150°C.
1200 варақи алюминий барои фурӯш
At temperatures above 125°C, the strength of 1200 aluminum alloy is higher than that of 7075 хӯлаи алюминий. The forming properties are relatively good in the hot state, annealed and newly quenched state and the heat treatment strengthening effect is remarkable, but the heat treatment process requirements are strict. The corrosion resistance is poor, but it can be effectively protected by cladding with pure aluminum; it is easy to produce cracks during welding, but it can be welded or riveted by a special process. Widely used in aircraft structures, парчинхо, truck hubs, propeller components, and various other structural parts.