5000 シリーズ合金アルマイト処理アルミニウム

とは何ですか 5000 シリーズ陽極酸化アルミニウム合金 ?

陽極 陽極酸化アルミニウム板を対応するアルミニウム電解液に配置します。 (硫酸など, クロム酸, シュウ酸, 等) 陽極として使用される, 特定の条件下での印象と現在の役割, 電気分解をする.

アルミニウム陽極酸化物 , 表面に酸化アルミニウムの薄い層を形成する, 厚さは 5 ～ 20 ミクロン, hard anode oxidation film is 60 ～ 200 ミクロン. After the anodic oxidation it improves its hardness and resistance to wear,can reaching 250-500 kg/square millimeter.Good heat resistance, hard anode oxidation film'smelting point is as high as 2320 K. good insulation, bear the breakdown voltage up to 2000 V, and enhance the corrosion resistance,not corroive in salt fog ω = 0.03 NaCl in thousands of hours.

Oxidation film thin layers having a large number of microporous,can adsorb lubricant, suit to make the engine cylinder or other wear parts; Microporous membrane adsorption ability can shade into kinds of beautiful and bright colors. Non-ferrous metal or its alloy (アルミニウムなどの, magnesium alloys, 等) can undertake anode oxidation processing.

Anodized aluminum widely used in mechanical parts, the plane automobile components, precision instrument and radio equipment, 建物の装飾, マシンシェル, ランプと照明, electronic consumer products, 手工芸品, 家庭用電化製品, 室内装飾, sign, 家具, automobile decoration etc.

5xxx anodized aluminum alloy performance characteristics

The good workability:anodic oxidation aluminum plate has high decorative performance, modest hardness, can be easily bending and forming. highly speed stamping continuity is convenient for directly processed into products,It do not need carry out complex surface treatment, greatly shorten production cycle and reduce production costs.

Good Weathering: anodic oxidation aluminum plate with standard thickness oxidation film (3μm) is used in long-term discoloration indoor, 腐食なし, not oxidation, no rust.Those with increasing Thick oxidation film (10 μm) can be used in outdoor , and long-term exposed to sunlight with discoloration.

Strong metal Feeling: the anodized aluminum has high surface hardness,coming to the gem grade,high resistance to scrape ,the surface not having paint covers, keeping aluminum metal color, improving the product level and added value.

What should be paid attention to in the oxidation of 5000 シリーズアルミニウム合金?

Alloys in the 5xxx series contain magnesium. When anodized, these alloys form a strong, transparent oxide layer as long as the magnesium alloy content remains within a certain percentage range.

の違い 5 series anodized aluminum and 6 シリーズ

5000 series anodized aluminum vs 6000 シリーズ陽極酸化アルミニウム

5XXX Series - Like the 3XXX series, this series is also a manganese alloy. After the anodizing process, the alloys in this series provide a clear, strong oxide layer, making them ideal for anodizing. These alloys are sometimes replaced by the 4XXX series alloys for weld filler metals. That's because the weld color matches the rest of the anodized aluminum assembly very well.

6XXX Series – This series was developed for aluminum alloys containing silicon and magnesium. Both of these alloys are excellent choices for anodizing. The oxide layer after anodizing is transparent and provides excellent protection. This family of alloys has desirable mechanical properties, is readily anodizable, and is the most common choice for structural applications.