What is an aluminum plate heat sink?
Most of the aluminum plate heat sinks are made of formed aluminum profiles as raw materials, deformed by an extrusion process, and then cast by welding, spraying, and other processes.
aluminum heat sink plate
Is aluminum sheet good for heat sink?
Common heat sink boards are copper and aluminum, as well as copper-aluminum composite boards. Although copper plate has good thermal conductivity, it is expensive, 柔らかい, heavy, and easy to oxidize. したがって, the aluminum plate is the preferred material for heat sinks, and the manufacturing process is relatively simple. Custom aluminum profiles are ideal for most heat sink applications and are the material of choice for heat sinks, offering significant price and processing advantages.
Traditional aluminum heat sink
What type of aluminum is used for heat sinks?
What material should the heat sink be made from?
Both copper and aluminum plates can be used as raw materials for heat sinks, and copper has very high thermal conductivity. しかし, the processing technology and price of copper are relatively high.
The most common radiator material is the aluminum alloy in the 6000 シリーズ, its high machinability and excellent plasticity make it possible to manufacture profile radiators by extrusion process. Mainly 6060 アルミシート, 6061 アルミシート, そして 6063 alloys and pure aluminum. Pure aluminum plate radiator has an excellent radiator effect, the heating effect. It is obviously more used in environments with high thermal conductivity requirements, such as hospital delivery rooms, nursing homes, private villas, 等, where there is a large demand for warmth.
heat sink sheet metal
Aluminum sheet heat sink advantage
1. Stable performance and long-term use
2. Hydraulic Linear Bearing Fine Cutting
3. Fine surface treatment
4. Good cooling effect
6061 aluminum plate heat sink chemical composition:
<tdCuMnMgCrZnTiotherAl<td0.15-0.400.150.8-1.20.04-0.350.250.150.15Allowance
| 要素 | そして | 鉄 |
| コンテンツ | 0.40-0.8 | 0.7 |
機械的性質 6061 aluminum plate heat sink:
Tensile strength σb (MPa): ≥180
Yield strength σ0.2 (MPa): ≥110
Elongation δ5 (%): ≥14